Stainless steel strip process

6Cr13 stainless steel strip:  Martensitic stainless steel, quenching hardness can reach

 HRC58. As an ideal material for high-end knives and scissors,  it can replace imported materials. Mainly application is for the razor blades, blades materials.

Stainless steel Strip Process:

1.     Electric furnace

2.  Ladle arc refining furnace

3.  Horizontal continuous casting

4.  Electricity slag remelting refining

5.  Forging molding

6.  Hot rolling steel strip

7.  Annealing

8.  Acid pickling

9.  Cold roll forming

10. Bright annealed

11. Precision cold rolled

12. Precision strip cutting

13. Packing

Grade: 6Cr13

Size: 0.1x15.4mm, 0.1x16.97mm, 0.1x22.4mm

Strips Thickness  Range: 0.095-0.100mm.

Strips  Width  Tolerance: 0.05mm.

Coil weight: 15-25kg

Hardness: HV 280-320

Application: To meet the needs of user, according to Swedish and other relevant technical requirements, our company developed the razor piece special stainless steel belt. After the examination, the chemical composition and mechanical properties such as hardness is accord with the requirement. The appearance quality and size deviation, surface quality and achieve user's requirements, batch production.